Decorative space interior decoration decoration design decoration company Low porosity clay bricks are made of low aluminum mullite as the main raw material, formed by high pressure molding and high temperature sintering. The main mineral composition is mullite phase, the product has excellent high temperature physical properties and chemical erosion resistance. Suitable for Plugging Oven Holes,Clogging Refractory Clay Bricks,Clogging Refractory Clay Brick Huixian Xinwei Refractories Co. , https://www.xinweirefractory.com
Low porosity clay brick stability is good, the degree of erosion does not occur sudden change, than ordinary clay brick life increased by 2 to 3 times. Thermal conductivity, specific heat and solubility, respectively, than ordinary clay bricks 2 times higher than 10% and 40%, heat storage capacity than ordinary clay bricks 50% to 60% higher than the thermal efficiency of the kiln can be improved.
Low porosity clay bricks are characterized by:
1. Low porosity, 13 to 15%;
2. Load softening temperature is high for about 1472 ℃;
3. High compressive strength at room temperature, generally about 100MPa;
4. Good volume stability at high temperature and good abrasion resistance;
5. good resistance to infiltration and erosion.
Low porosity clay brick as a good clay refractory brick products, so often used in chemical erosion, temperature fluctuations in the environment, such as steel, glass, chemical industry. The effect is quite obvious in the use of glass hot room and the use of iron water tank.
Asia Pacific Space Art Design Competition opens
Passion creates a dream and design leads China. Sponsored by China Building Decoration Association, organized by China Building Decoration Association Design Committee, 2010 Asia Pacific Space Environment Art Design Competition (China Qualifiers) co-organized by Tsinghua University Academy of Fine Arts and Italian Bees Tiles and China Indoor Space Environment Art Design Competition 2009 Shanghai Press Release The meeting and the forum were held on the afternoon of the 2nd of this month at the Shanghai International Convention Center.
Ding Qi, deputy director of the China Hotel Association's Design and Decoration Committee, presided over the meeting. Tian Dechang, secretary general of the Design Committee of the China Building Decoration Association, Wang Yang, secretary general of the design committee of the Shanghai Decoration and Decoration Industry Association, and Gao Shengli, vice chairman of the Italian Bee Ceramics Tiles, respectively addressed the meeting. Secretary General Tian Dechang issued letters of appointment to four expert judges including Wang Yang, Lai Zengxiang, Shi Nanqiao and Yang Wenjia. Yang Wenjia, former editor-in-chief of Interior Design and Decoration Magazine, Yu Guomin, Dean of Hangzhou Gomez Architecture Design and Design Institute, Sun Tianwen, Chief Designer of Shanghai Black Bubble Architectural Design Company, and Song Weijian, Chairman of Shanghai Weijian Architectural Space Design Co., Ltd. The keynote speech and the final of the forum are on-site interactions.
At this meeting, more than 20 media reporters went to report.